The ingrdient of the brick earth which enables the brick to retain shape is
Silica (50% to 60%): It prevents raw bricks from shrinking, warping, and cracking during drying and burning. This
stabilizes the bricks so they can retain their shape.
Alumina (20% to 30%): It imparts plasticity to the brick earth, which allows it to be easily molded into a brick shape in its
wet state. However, it does not help retain that shape; an excess of alumina causes severe shrinkage and cracking
during drying.
Iron oxide (5% to 6%): Its primary role is to give the classic red color to the bricks and act as a flux to bind particles.
Magnesia (Less than 1%): It reduces overall shrinkage and lends a minor yellowish tint to the burnt brick product.
सिलिका (50% से 60%): यह कच्ची ईंटों को सूखने और पकने के दौरान सिकुड़ने, टेढ़ा होने और चटकने से रोकता है। यह ईंटों को स्थिर
रखता है, जिससे वे अपना आकार बनाए रख पाती हैं।
एल्युमिना (20% से 30%): यह ईंट बनाने वाली मिट्टी को लचीलापन (प्लास्टिसिटी) देता है, जिससे गीली अवस्था में उसे आसानी से ईंट का
आकार दिया जा सकता है। हालाँकि, यह उस आकार को बनाए रखने में मदद नहीं करता; एल्युमिना की अधिक मात्रा होने पर, सूखने के दौरान
ईंटें बहुत ज़्यादा सिकुड़ सकती हैं और उनमें दरारें आ सकती हैं।
आयरन ऑक्साइड (5% से 6%): इसका मुख्य काम ईंटों को उनका पारंपरिक लाल रंग देना और कणों को आपस में जोड़ने के लिए एक
'फ्लक्स' (जोड़ने वाले पदार्थ) के रूप में कार्य करना है।
मैग्नेशिया (1% से कम): यह ईंटों के सिकुड़ने की मात्रा को कम करता है और पकने के बाद ईंटों में हल्का पीलापन ला देता है।